 WC-48 Mylar® Type WC 48 Gauge Thickness Film List Price QUOTE
|
WC-75 Mylar® Type WC 75 Gauge Thickness Film List Price QUOTE
|
WC-92 Mylar® Type WC 92 Gauge Thickness Film List Price QUOTE
|
WC-142 Mylar® Type WC 142 Gauge Thickness Film List Price QUOTE
|
WC-200 Mylar® Type WC 200 Gauge Thickness Film List Price QUOTE
|
|||||
| Description | Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling characteristics. | |||||||||
| Thickness | 48 gauge | 75 gauge | 92 gauge | 142 gauge | 200 gauge | |||||
| Width | ||||||||||
| Length | ||||||||||
| Dielectric Strength | 2.8 kV | 3.5 kV | 4.0 kV | 5.5 kV | 7.7 kV | |||||
| Test Method for Dielectric Strength | American Society for Testing and Materials (ASTM) D149 1/4" electrode 500 V/sec 25ºC in air | |||||||||
| Optical Haze | 4 % | 15 % | 16 % | 18 % | 24 % | |||||
| Test Method for Optical Haze | American Society for Testing and Materials (ASTM) D1003 | |||||||||
| Elongation at Break (Machine Direction (MD)) | 110 % | 110 % | 110 % | 125 % | 135 % | |||||
| Test Method for Elongation at Break (Machine Direction (MD)) | American Society for Testing and Materials (ASTM) D882A | |||||||||
| Elongation at Break (Transverse Direction (TD)) | 70 % | 90 % | 90 % | 100 % | 110 % | |||||
| Test Method for Elongation at Break (Transverse Direction (TD)) | American Society for Testing and Materials (ASTM) D882A | |||||||||
| Tensile Strength (Machine Direction (MD)) | 26 kpsi | 28 kpsi | 28 kpsi | 28 kpsi | 28 kpsi | |||||
| Test Method for Tensile Strength (Machine Direction (MD)) | American Society for Testing and Materials (ASTM) D882A | |||||||||
| Tensile Strength (Transverse Direction (TD)) | 32 | 34 | 34 | 34 | 33 | |||||
| Test Method for Tensile Strength (Transverse Direction (TD)) | American Society for Testing and Materials (ASTM) D882A | |||||||||
| Nominal Yield | 41300 in²/lb | 26500 in²/lb | 21800 in²/lb | 14000 in²/lb | 9900 in²/lb | |||||
| Shrinkage (Machine Direction (MD)) at 150 Degree Celsius (ºC) Temperature | 2.0 % | 2.0 % | 1.9 % | 1.5 % | 1.3 % | |||||
| Test Method for Shrinkage (Machine Direction (MD)) at 150 Degree Celsius (ºC) Temperature | Unrestrained at 150ºC/30 min | |||||||||
| Shrinkage (Transverse Direction (TD)) at 150 Degree Celsius (ºC) Temperature | 1.0 % | 1.1 % | 1.1 % | 1.0 % | 0.8 % | |||||
| Test Method for Shrinkage (Transverse Direction (TD)) at 150 Degree Celsius (ºC) Temperature | Unrestrained at 150ºC/30 min | |||||||||
| Core Inside Diameter1 | 3 in | |||||||||
| Roll Outside Diameter | 13 in | |||||||||
| Core Inside Diameter (Master Roll) | 10 in | |||||||||
| Weight | ||||||||||
| Approvals | Underwriters Laboratories (UL 94 VTM-2) Underwriters Laboratories (UL) Recognition - MIL-I631D, TYPE G | |||||||||
| General Information | Mylar® Type WC films combine the tensile strength, dimensional stability, and dielectric strength needed for wire and cable applications. | |||||||||
| Special Features |
Slit rolls are available in the following ID and OD configuration:
|
|||||||||
| Typical Applications | Mylar® WC films possess the characteristics required for wire and cable used in the telecommunications and power transmission fields. | |||||||||
| Note | Custom Width available RFQ. | |||||||||
|
||||||||||